[en] YBa2Cu3O7-δ thick films have been deposited onto Ag substrates by the Electrophoretic Deposition (EPD) technique. Different microstructures and electrical behaviours were observed depending on the starting powder. Coatings prepared from commercial powder displayed significant porosity and the superconducting transition width was found to be magnetic-field dependent. Films produced from home-made coprecipitated powder are denser but contain some secondary phases. No dependence of the resistive transition as a function of magnetic field (H ≤ 20 Oe) was observed in that case.
Research Center/Unit :
SUPRATECS - Services Universitaires pour la Recherche et les Applications Technologiques de Matériaux Électro-Céramiques, Composites, Supraconducteurs - ULiège
Disciplines :
Chemistry Electrical & electronics engineering
Author, co-author :
Dusoulier, Laurent; Université de Liège - ULiège > Département de chimie (sciences) > Chimie inorganique structurale
Denis, Samuel; Royal Military Academy of Belgium and University of Liege > Département d'électricité, électronique et informatique (Montefiore) / CISS
Fagnard, Jean-François ; Université de Liège - ULiège > Dép. d'électric., électron. et informat. (Inst.Montefiore) > Capteurs et systèmes de mesures électriques
Henrist, Catherine ; Université de Liège - ULiège > Département de chimie (sciences) > Chimie inorganique structurale
Vanderheyden, Benoît ; Université de Liège - ULiège > Dép. d'électric., électron. et informat. (Inst.Montefiore) > Electronique et microsystèmes
Vanderbemden, Philippe ; Université de Liège - ULiège > Dép. d'électric., électron. et informat. (Inst.Montefiore) > Capteurs et systèmes de mesures électriques
Rulmont, André ; Université de Liège - ULiège > Département de chimie (sciences) > Département de chimie (sciences)