Effects of production and curing conditions on performances of stabilized compressed earth blocks: Kaolinite vs quartz-rich materials

This study investigated the effect of production and curing parameters on the mechanical performance of compressed earth blocks (CEBs) stabilized with 0-20 wt % CCR (calcium carbide residue). Kaolinite (K) and quartz (Q)­rich earthen materials were mixed with the CCR and used to mould CEBs at optimum moisture content (OMC) and OMC+2 % of the dry mixtures, cured at 20 °C, ambient temperature in the lab (30±5 °C) and 40 °C for 0-90 days. After curing, the reactivity of the materials and compressive strength of dry CEBs were tested. Increasing the moulding moisture from OMC to OMC+2 decreased the compressive strength 0.3 times (4.4 to 3.3 MPa) for the CEBs stabilized with 20 % CCR cured at 30±5 °C for 45 days. Similarly, the compressive strength (4.4 MPa) was reached by CEBs stabilized with 10 and 20 % CCR after 28 and 45 days of curing, respectively. At 40 °C, the compressive strength increased 3.3 times (1.1 to 4.7 MPa with 0 to 20 % CCR) for K-rich and 2.5 times (2 to 7.1 MPa) for Q˗rich materials. At 20 °C, the compressive strength increased only 1.3 times (1.1 to 2.5 MPa) for K˗rich and barely 0.7 times (2 to 3.4 MPa) for Q-rich materials. These suggest that CCR is useful for stabilization and improving the performances of CEBs in hot regions.