[en] The NaF-AlF(3) system with additions of CaF(2) and MgF(2) has been studied with Raman and vapor pressure measurements for 3 >/= CR (NaF/AlF(3) molar ratio) >/= 1 and up to 50 mol % additive. The results show that the binary melt can be described using the two equilibria AlF(6)(3)(-) = AlF(6)(2)(-) + F(-) and AlF(5)(2)(-) = AlF(4)(-) + F(-) with equilibrium constants 0.25 and 0.05, respectively, at 1293 K. Both reactions have positive reaction enthalpies. The first equilibrium is strongly shifted to the right resulting in a melt mixture with very low AlF(6)(3)(-) concentrations even at the Na(3)AlF(6) composition. Evidence for nonideal mixing of anions was found. For the ternaries, models based on Raman data are presented and compared with vapor pressure measurements. Good agreement is observed when association between the additives, CaF(2) or MgF(2), with the AlF(5)(2)(-) ions in the melt was considered. This association could be experimentally observed through a band broadening and a slight shift in the AlF(5)(2)(-) band frequency. Our vapor pressures and Raman data both indicate that MgF(2) clearly acts as an acid when added to NaF-AlF(3) melts of any composition. When CaF(2) is added, a slight decrease of vapor pressure occurs. Raman data indicate a decrease of AlF(4)(-) concentration, corresponding to a dissociation of CaF(2) with liberation of F(-) ions. All these results are, however, very much dependent on the initial melt composition. These data are explained in terms of acid-base, dilution, and association reactions of the solute with the solvent.
Disciplines :
Chemistry
Author, co-author :
Gilbert, Bernard ; Université de Liège - ULiège > Chimie analytique et électrochimie
Robert, Eric; Université de Liège - ULiège
Tixhon, Eric; Université de Liège - ULiège
Olsen, J. E.
Ostvold, T.
Language :
English
Title :
Structure and Thermodynamics of Naf-Alf(3) Melts with Addition of Caf(2) and Mgf(2)
Publication date :
03 July 1996
Journal title :
Inorganic Chemistry
ISSN :
0020-1669
eISSN :
1520-510X
Publisher :
American Chemical Society, United States - District of Columbia
Irish, D. E.; Ozeki, T. Analytical Roman Spectroscopy. Chemical Analysis; Wiley Interscience: New York, 1991; p 59.
Dewing, E. W. Metall. Trans. 1989, 20B, 675.
Gilbert, B.; Robert. E.; Tixhon, E.; Olsen, J. E.; Østvold, T. Light Met. 1995, 181.
Foster, P. A.; Frank, W. B. J. Electrochem. Soc. 1960, 107, 997.
Dewing, E. W. Metall. Trans. 1990, 21B, 285.
Sterten, Aa.; Mæland, I. Acta Chem. Scand. 1985, A39, 241.
Grjotheim, K.; Krohn, C.; Malinovský, M.; Matiasovskaý, K.; Thonstad, J. Aluminium Electrolysis. Fundamentals of the Hall-Héroult Process; Aluminium-Verlag: Dësseldorf, Germany, 1982; p 97.
Rolin, M.; Bernard, M. Bull. Soc. Chim. Fr. 1962, 429.
Rolin, M.; Rey, M. Bull Soc. Chim. Fr. 1966, 2785.
Gilbert, B.; Begun, G. M.; Mamantov, G. J. Chem. Phys. 1975, 62, 950.
Gilbert, B.; Materne, T. Appl. Spectrosc. 1990, 44, 299.
Dewing, E. W. In Proceedings of the Fifth International Symposium on Molten Salts; Saboungi, M. L., Newman, D. S., Johnson, K., Inman, D., Eds.; The Electrochemical Society Proceedings 86; The Electrochemical Society: New York, 1986.
Hertzberg, T. Modfit - A general computer program for nonlinear parameter estimation. Institute of Chemical Engineering, University of Trondheim, NTH, Norway, 1983.
Knapstad, B.; Linga, H.; Øye, H. A. Ber. Bunsen-Ges Phys. Chem. 1981, 85, 1132.
Kvande, H. Thesis, Institute of Inorganic Chemistry. NTH, University of Trondheim, Norway, 1979.
Guzman, J. Thesis, Institute of Inorganic Chemistry, NTH, University of Trondheim, Norway, 1986.
Guzman, J.; Grjotheim, K.; Østvold, T. Light Met. 1986, 425.
Zhou, H.; Herstad, O.; Østvold, T. Light Met. 1991, 511.
Temkin, M. Acta Physiochim. 1945, 20, 411.
Brooker, M. H. Proceedings from the H. A. Øye Symposium; NTH: Trondheim, Norway, 1995, pp 431-434.
Ratkje, S. K.; Cyvin, S. J.; Hafskjold, B. Appl. Spectrosc. 1993, 47, 375.
Brooker, M. H. Private communication.
Hawthorne, F. C.; Ferguson, R. B. Can. Mineral. 1975, 13, 377.
Jacobini, C.; Leble, A.; Rousseau, J. J. J. Solid Stale Chem. 1981, 36, 297.
Zhou, H. Thesis, Institute of Inorganic Chemistry, NTH, University of Trondheim, Norway, 1991.
Papatheodorou, G. N. J. Chem. Phys. 1977, 66, 2893.
Hong, K. C.; Kleppa, O. J. J. Phys. Chem. 1978, 82, 176.
JANAF Thermochemical Tables 1985, 14.
Dewing, E. W.; van der Kouwe, E. Th. Light Met. 1989, 297.