Management of root perforations using MTA with or without Er:YAG laser irradiation: An in vitro study

[en] The aim of this in vitro study is to compare the microleakage of a root perforation sealed with MTA (mineral trioxide aggregate) (group M) to that sealed with MTA following Er:YAG laser irradiation (group ML). Forty-two recently extracted human monoroot teeth were used. Two cavities were prepared on each root surface. Randomly, on each root, the exposed dentine of one cavity was irradiated prior to MTA filling using an Er:YAG laser with the following settings: 200 mJ/pulses under an air water spray, 10Hz, pulse duration of 50sec, and 0.7mm beam diameter. All cavities were then sealed with MTA. submitted to thermocycling and immersed in 2 methylene blue dye solution for 12h. The penetration of methylene blue in the microleakage of cavity was observed and recorded. The mean value dye penetration in cavities sealed with MTA following Er:YAG laser irradiation (23.91 14.63 ) was lower than that of unlased cavities sealed only with MTA (25.17 17.53 ). No significant difference was noted. The use of an Er:YAG laser beam for dentinal conditioning prior to MTA filling of perforated roots did not decrease significantly the microleakage of MTA sealing when compared to the conventional use of MTA filling. Copyright © 2012 M. Tielemans et al.

Disciplines :

Dentistry & oral medicine

Author, co-author :

Tielemans, Marc

Saloukas, I.; Department of Dental Sciences, Faculty of Medicine, University of Lige, 4000 Lige, Belgium

Heysselaer, D.; Unit of Ultrastructural Morphology, Laboratory of Evolutive and Functional Morphology, University of Lige, 4000 Lige, Belgium

Compère, Philippe ; Université de Liège - ULiège > Département de Biologie, Ecologie et Evolution > Département de Biologie, Ecologie et Evolution

Nyssen-Behets, C.; L'Unité de Morphologie Expérimrntale, Université Catholique de Louvain, 1200 Bruxelles, Belgium

Namour, Samir ; Université de Liège - ULiège > Département de sciences dentaires > Département de sciences dentaires

Language :

English

Title :

Management of root perforations using MTA with or without Er:YAG laser irradiation: An in vitro study

Publication date :

2012

Journal title :

International Journal of Dentistry

ISSN :

1687-8728

eISSN :

1687-8736

Publisher :

Hindawi Publishing Corporation, Egypt

Peer reviewed :

Peer Reviewed verified by ORBi

Available on ORBi :

since 11 July 2014

Statistics

Number of views

85 (4 by ULiège)

Number of downloads

212 (1 by ULiège)

More statistics

Scopus citations^®

Scopus citations^®
without self-citations

OpenCitations

OpenAlex citations

Bibliography

Lee S. J., Monsef M., Torabinejad M., Sealing ability of a mineral trioxide aggregate for repair of lateral root perforations Journal of Endodontics 1993 19 11 541 544
Torabinejad M., Higa R. K., McKendry D. J., Pitt Ford T. R., Dye leakage of four root end filling materials: effects of blood contamination Journal of Endodontics 1994 20 4 159 163
Torabinejad M., Pitt Ford T. R., McKendry D. J., Abedi H. R., Miller D. A., Kariyawasam S. P., Histologic assessment of mineral trioxide aggregate as a root-end filling in monkeys Journal of Endodontics 1997 23 4 225 228 (Pubitemid 127730586)
Tang H. M., Torabinejad M., Kettering J. D., Leakage evaluation of root end filling materials using endotoxin Journal of Endodontics 2002 28 1 5 7
Parirokh M., Torabinejad M., Mineral trioxide aggregate: a comprehensive literature review-part III: clinical applications, drawbacks, and mechanism of action Journal of Endodontics 2010 36 3 400 413
Mente J., Hage N., Pfefferle T., Koch M. J., Geletneky B., Dreyhaupt J., Martin N., Staehle H. J., Treatment outcome of mineral trioxide aggregate: repair of root perforations Journal of Endodontics 2010 36 2 208 213
Main C., Mirzayan N., Shabahang S., Torabinejad M., Repair of root perforations using mineral trioxide aggregate: a long-term study Journal of Endodontics 2004 30 2 80 83 (Pubitemid 38650755)
Torabinejad M., Ford T. R., Abedi H. R., Kariyawasam S. P., Tang H. M., Tissue reaction to implanted root-end filling materials in the tibia and mandible of guinea pigs Journal of Endodontics 1998 24 7 468 471
Fournier P., Bouter D., Obturation biomaterials in retrograde endodontic microsurgery Revue D'odonto-Stomatologie 2005 34 3 173 192
Torabinejad M., Hong C. U., McDonald F., Pitt Ford T. R., Physical and chemical properties of a new root-end filling material Journal of Endodontics 1995 21 7 349 353
Gondim E., Kim S., de Souza-Filho F. J., An investigation of microleakage from root-end fillings in ultrasonic retrograde cavities with or without finishing: a quantitative analysis Oral Surgery, Oral Medicine, Oral Pathology, Oral Radiology and Endodontology 2005 99 6 755 760 (Pubitemid 40719338)
Raldi D. P., Mello I., Neves A. C. C., Habitante S. M., Miyagi S. S. P., Lage-Marques J. L., Attachment of cultured fibroblasts and ultrastructural analysis of simulated cervical resorptions treated with high-power lasers and MTA Oral Surgery, Oral Medicine, Oral Pathology, Oral Radiology and Endodontology 2010 109 2 e154 e161
Baraba A., Miletic I., Krmek S. J., Perhavec T., Bozic Z., Anic I., Ablative potential of the erbium-doped yttrium aluminium garnet laser and conventional handpieces: a comparative study Photomedicine and Laser Surgery 2009 27 6 921 927
Delmé K., Meire M., De Bruyne M., Nammour S., De Moor R., Cavity preparation using an Er:YAG laser in the adult dentition Revue Belge de Médecine Dentaire 2009 64 2 71 80
Starkey D. L., Anderson R. W., Pashley D. H., An evaluation of the effect of methylene blue dye pH on apical leakage Journal of Endodontics 1993 19 9 435 439
Carvalho C. A., Valera M. C., Gown-Soares S., De Paula Eduardo C. D., Effects of Nd:YAG and Er:YAG lasers on the sealing of root canal fillings Journal of Clinical Laser Medicine and Surgery 2002 20 4 215 219 (Pubitemid 34848176)
Gouw-Soares S., Stabholz A., Lage-Marques J. L., Zezell D. M., Groth E. B., Eduardo C. P., Comparative study of dentine permeability after apicectomy and surface treatment with 9.6 m TEA CO 2 and Er:YAG laser irradiation Journal of Clinical Laser Medicine and Surgery 2004 22 2 129 139 (Pubitemid 38679928)
Folwaczny M., Aggstaller H., Mehl A., Hickel R., Removal of bacterial endotoxin from root surface with Er:YAG laser American Journal of Dentistry 2003 16 1 3 5 (Pubitemid 41309977)
Bertrand M. F., Hessleyer D., Muller-Bolla M., Nammour S., Rocca J. P., Scanning electron microscopic evaluation of resin-dentin interface after Er:YAG laser preparation Lasers in Surgery and Medicine 2004 35 1 51 57 (Pubitemid 39063256)
Curti M., Rocca J. P., Bertrand M. F., Nammour S., Morpho-structural aspects of Er:YAG-prepared class V cavities Journal of Clinical Laser Medicine and Surgery 2004 22 2 119 123 (Pubitemid 38679926)
Garthner A. H., Dorn S. O., Advances in endodontis surgery Dental Clinics of North America 1992 36 2 357 378
Duarte M. A. H., De Oliveira Demarchi A. C. C., Yamashita J. C., Kuga M. C., De Campos Fraga S., Arsenic release provided by MTA and Portland cement Oral Surgery, Oral Medicine, Oral Pathology, Oral Radiology and Endodontology 2005 99 5 648 650 (Pubitemid 40522504)
Tselnik M., Craig Baumgartner J., Gordon Marshall J., Bacterial leakage with mineral trioxide aggregate or a resin-modified glass ionomer used as a coronal barrier Journal of Endodontics 2004 30 11 782 784 (Pubitemid 39481784)
Asrari M., Lobner D., In vitro neurotoxic evaluation of root-end-filling materials Journal of Endodontics 2003 29 11 743 746 (Pubitemid 38650795)
Economides N., Pantelidou O., Kokkas A., Tziafas D., Short-term periradicular tissue response to mineral trioxide aggregate (MTA) as root-end filling material International Endodontic Journal 2003 36 1 44 48 (Pubitemid 37243853)
Camilleri J., Montesin F. E., Papaioannou S., McDonald F., Pitt Ford T. R., Biocompatibility of two commercial forms of mineral trioxide aggregate International Endodontic Journal 2004 37 10 699 704 (Pubitemid 39296578)
Fridland M., Rosado R., Mineral trioxide aggregate (MTA) solubility and porosity with different water-to-powder ratios Journal of Endodontics 2003 29 12 814 817 (Pubitemid 38659649)
Mitchell P. J. C., Pitt Ford T. R., Torabinejad M., McDonald F., Osteoblast biocompatibility of mineral trioxide aggregate Biomaterials 1999 20 2 167 173 (Pubitemid 29041344)
Koh E. T., McDonald F., Pitt Ford T. R., Torabinejad M., Cellular response to mineral trioxide aggregate Journal of Endodontics 1998 24 8 543 547 (Pubitemid 128704247)
Pitt Ford T. R., Andreasen J. O., Dorn S. O., Kariyawasam S. P., Effect of various zinc oxide materials as root-end fillings on healing after replantation International Endodontic Journal 1995 28 6 273 278
Thomson T. S., Berry J. E., Somerman M. J., Kirkwood K. L., Cementoblasts maintain expression of osteocalcin in the presence of mineral trioxide aggregate Journal of Endodontics 2003 29 6 407 412 (Pubitemid 41582824)
Felippe W. T., Felippe M. C. S., Rocha M. J. C., The effect of mineral trioxide aggregate on the apexification and periapical healing of teeth with incomplete root formation International Endodontic Journal 2006 39 1 2 9 (Pubitemid 43432889)
Holland R., Mineral trioxide aggregate repair of lateral root perforations Journal of Endodontics 2001 27 4 281 284 (Pubitemid 33753623)
Fuss Z., Trope M., Root perforations: classification and treatment choices based on prognostic factors Endodontics and Dental Traumatology 1996 12 6 255 264 (Pubitemid 126796319)
Karlovic Z., Pezelj-Ribaric S., Miletic I., Jukic S., Grgurevic J., Anic I., Erbium:YAG laser versus ultrasonic in preparation of root-end cavities Journal of Endodontics 2005 31 11 821 823 (Pubitemid 41578794)
Crespi R., Barone A., Covani U., Effect of Er:YAG laser on diseased root surfaces: an in vivo study Journal of Periodontology 2005 76 8 1386 1390 (Pubitemid 41245785)