[en] Ballast tanks are of great importance in the lifetime of modern merchant ships. Making a ballast tank less susceptible to corrosion can, therefore, prolong the useful life of a ship and, thereby, lower its operational cost. An option to reinforce a ballast tank is to construct it out of a corrosion-resistant steel type. Such steel was recently produced by POSCO Ltd., South Korea. After 6 months of permanent immersion, the average corrosion rate of A and AH steel (31 samples) was 535 g m−2 year−1, while the Korean CRS was corroding with 378 g m−2 year−1. This entails a gain of 29 %. Follow-up measurements after 10, 20, and 24 months confirmed this. The results after 6 months exposure to alternating wet/dry conditions are even more explicit. Furthermore, the physical and metallurgical properties of this steel show a density of 7.646 t/m3, the elasticity modulus 209.3 GPa, the tensile strength 572 MPa, and the hardness 169HV10. Microscopically, the metal consists of equiaxed and recrystallized grains (ferrite and pearlite), with an average size of between 20 and 30 µm (ASTM E 112—12 grain size number between 7 and 8) with a few elongated pearlitic grains. The structure is banded ferrite/pearlite. On the basis of a series of energy dispersive X-ray spectrometer measurements the lower corrosion rate of the steel can be attributed to the interplay of Al, Cr, their oxides, and the corroding steel. In addition, the role of each element in the formation of oxide layers and the mechanisms contributing to the corrosion resistance are discussed.
IMO (2006) Performance standard for protective coatings for dedicated seawater ballast tanks in all types of ships and double-side skin spaces of bulk carriers. IMO, MSC.215(82)
IACS (2006) Guidelines for coating maintenance & repairs for ballast tanks and combined cargo/ballast tanks on oil tankers. IACS, Rec. 87/Rev. 1
De Baere K, Verstraelen H, Rigo P, Van Passel S, Lenaerts S, Potters G (2013) Study on alternative approaches to corrosion protection of ballast tanks using an economic model. Mar Struct 32:1–17
Walton O (2005) Making modern shipping: making the modern world. A concise history of modern commercial shipping. In: The Britannia Steam Ship Insurance Association Limited 150th anniversary, p 8
IMO (2000) Tanker familiarization course, model 1.01. IMO, London
NN (2011) Nippon Steel’s NSGP-1 approved for oil tanker cargo tank’s bottom plate. Japan Metal Bulletin: http://www.japanmetalbulletin.com. Accessed 4 May 2016
Shiotani K, Samusawa I, Tachibana S, Komori T (2012) Development of corrosion resistant steel for ballast tank. In: Proceedings international conference on developments in ship design & construction (ICSOT), pp 27–33
ASTM (2007) Standard test methods for notched bar impact testing of metallic materials. ASTM 23
European Committee for standardization (1990) Metallic materials: Charpy impact test. EN 10 045
Perlibakas V (2004) Distance measures for PCA-based face recognition. Pattern Recognit Lett 25:711–724
Croux C, Ruiz-Gazen A (2005) High breakdown estimators for principal components: the projection-pursuit approach revisited. J Multivar Anal 95(1):206–226
R Development Core Team (2011) The R Project for statistical computing. Institute for Statistics and Mathematics of the WU, Wien
Maechler M, Rousseeuw P, Struyf A, Hubert M, Hornik K (2012) Cluster: Cluster analysis basics and extensions. R Package
Filzmoser P, Fritz H, Kalcher K (2014) pcaPP: Robust PCA by Projection Pursuit. R Package 1:9–60
Koenker R (2016) quantreg: Quantile Regression. R Package
Kasuya T (2007) Carbon equivalent to assess hardenability of steel and prediction of haz hardness distribution. Nippon Steel Technical Report nr. 95
Hinton RW, Wiswesser RK (2008) Estimating welding preheat requirements for unknown grades of carbon and low-alloy steels. Weld J 87:273–278
NN (2011) Carbon equivalents and transformation temperature. The Japan Welding Engineering Society, Tokyo, Japan
ASM (1997) Weld integrity and performance. ASM International, Almere, The Netherlands
ISO (2003) Destructive tests on welds in metallic materials—macroscopic and microscopic examination of welds. ISO 17639
ISO (2007) Welding—fusion welded joints in steel, nickel, titanium and their alloys (beam welding excluded)—quality levels of inspection. NEN-EN-ISO 5817
Shackelford JF (2005) Introduction to materials science for engineers, 6th edn. Pearson Education Inc, New York, USA
Kopeliovich D (2012) Substances and technologies, knowledge source on materials engineering. Correspondence to the author, December 5, 2012, http://www.substech.com. Accessed 4 May 2016
Templeton JS III (2006) Offshore technology in civil engineering. American Society of Civil Engineers, Reston
Lampman S (1997) weld integrity and performance. source book adapted from ASM International Handbooks. In: Conference Proceedings and Technical Books, ASM International
Smet JP (2000) Lastechniek. Unpublished course, University of Antwerp, Faculty Applied Engineering. Antwerpen, Belgium
Aloraier A et al (2010) Weld repair practices without post weld heat treatment for ferritic alloys and their consequences on residual stresses: a review. Int J Press Vessels Pip 87(4):127–133
Laha K et al (2009) Type IV cracking susceptibility in weld joints of different grades of Cr-Mo ferritic steel. Metall Mater Trans A 40(2):386–397
Bureau Veritas (2011) Mechanical properties of carbon steel, materials and weldings, Chapter 2, steel and iron products, section 1, Rolled steel plates, sections and bars, article 2, normal and higher strength structural steels. Bureau Veritas
Elert G (2004) The physics fact book, density of steel. Private communication, 2013, http://hypertextbook.com/facts/2004/KarenSutherland.shtml. Accessed 4 May 2016
IACS (2005) Common Structural Rules. http://www.iacs.org.uk/publications/CommonRulePublications.aspx?pageid=4§ionid=2. Accessed 4 May 2016
VanDerhorn E, Wang G (2011) Sustainable maritime transportation and exploitation of sea resources, chapter 44: a statistical study on the material properties of shipbuilding steels. CRC, pp 371–378
NN (2001) Datasheet A 3.5, Lloyd’s ship hull steel—normal and higher strength steel plate for hull construction. Arcelor Mittal
Lloyds Register (2001) Rules and regulations set appropriate standards for the design, construction and lifetime maintenance of ships. Lloyds Register
JFE Steel Corporation (s.d.) Steel Plate, Catalogue No. C1E–001-07, 44 p. http://www.jfe-steel.co.jp/en/products/plate/catalog/c1e-001.pdf. Accessed 10 Feb 2016
Nippon Steel and Sumimoto Metal Corp. (2014) Cor-Ten™, 32 p., https://www.nssmc.com/product/catalog_download/pdf/A006en.pdf. Accessed 10 Feb 2016
Pleshivtsev VG et al (2009) Effect of carbon content and stressed state on the corrosion rate of pipe steel in heating systems. Metallurgist 53(7–8):502–505
Nesic S, Lunde L (1993) CO2 Corrosion of carbon steel in two-phase flow. In: NACE Conference: nr. 640
Campbell FC (2008) Elements of metallurgy and engineering alloys. ASM International, Almere, The Netherlands, pp 14
Morris JW Jr (2001) The influence of grain size on the mechanical properties of steel. In: International symposium on ultra-fine grained steels Tokyo, Japan
NN (1987) Modern steels and their properties. Akron Steel Treating Company, Ohio, USA
MacDougall Graham (2002) Growth and stability of passive films, corrosion mechanisms in theory and practice, 2nd edn. Marcel Dekker, Basel, p 627
Marcus P, Olefjord I (1988) A round robin on combined electrochemical and AES/ESCA characterization of the passive films on Fe-Cr and Fe-Cr-Mo alloys. Corros Sci 28(6):589–602
Schweitzer A (2007) Fundamentals of metallic corrosion. CRC, Boca Raton, Florida, USA, pp 750
Roberge P (2000) Handbook of corrosion engineering. McGraw-Hill, pp 1138
Asphahani AI (1987) Corrosion of nickel-base alloys. In: Metals handbook: corrosion. ASM International, Almere, The Netherlands, pp 641–657
Ahmad Z (2006) Principles of corrosion engineering and corrosion control. Elsevier Science & Technology Books, Amsterdam, The Netherlands, pp 672
The European Stainless Steel Association, correspondence to the author, December 5, 2012, http://www.euro-inox.org. Accessed 4 May 2016
Mukherjee KP et al. (1958) Effect of low alloy additions on corrosion of steel in different atmospheres. In: Symposium on production, properties and applications of alloy and special steels, pp 425–433
Melchers RE (2004) Effect of small compositional changes on the marine immersion corrosion of low alloy steels. Corros Sci 46(7):1669–1691
Lankford WT Jr (1985) The making, shaping and treating of steel. Assoc Iron Steel Eng 10:1572
Boyer HE, Gall TL (1985) Metals handbook. ASM International, Almere, The Netherlands, p 950
Potemkin DK et al (1970) Surface decarburizing during the production of rolled steel. Metallurgist 14(2):127–130
Lopez DA et al (2003) The influence of carbon steel microstructure on corrosion layers: an XPS and SEM characterization. Appl Surf Sci 207(1):69–85
Yamashita M (2000) Quantitative analysis of ultra-fine goethite in rust layer on steel using Moessbauer and X-ray diffraction spectroscopy. J Jpn Inst Met 64(1):77–78
Zhang QC et al (2003) Corrosion behavior of weathering steel in marine environment. Mater Chem Phys 77(2):603–608
Yamashita M et al (2004) Nanostructure of protective rust layer on weathering steel examined using synchrotron radiation X-rays. Mater Trans 45(6):1920–1924
Sakashita S, Shiotani K, Kashima K, Murakoshi S, Fukunaga K, Baba T, Takai A, Takada A, Osawa N (2015) Onboard study on deterioration of coated steel in water ballast tank. In: Proceedings of the twenty-fifth (2015) international ocean and polar engineering conference Kona, Big Island, Hawaii, USA, June 21–26, 2015, pp 521–527
Kimura M et al (2003) Corrosion protection mechanism of the advanced weathering steel (Fe-3.0Ni-0.40Cu) in a coastal area. In: Asian-Pacific Corrosion Control Conference, Abs 740
Tamura H (2008) The role of rusts in corrosion and corrosion protection of iron and steel. Corros Sci 50(7):1872–1883
Nagayama M, Cohen M (1962) The anodic oxidation of iron in a neutral solution, the nature and composition of the passive film. J Electrochem Soc 109:781–790
Saha JH (2013) Corrosion of constructional steels in marine and industrial environment. Springer, New York, USA, pp 173
Hara S, Kamimura T, Miyuki H, Yamashita M (2007) Taxonomy for protective ability of rust layer using its composition formed on weathering steel bridge. Corros Sci 49(3):1131–1142
Kamimura T et al (2006) Composition and protective ability of rust layer formed on weathering steel exposed to various environments. Corros Sci 48(9):2799–2812
Dunn DS et al (2000) Corrosion of iron under alternating wet and dry conditions. Corrosion 56(5):470–481
Sato N (2011) Basics of Corrosion Chemistry. In: Sharma SK (eds) Green Corrosion Chemistry and Engineering: Opportunities and Challenges. Wiley, Germany. doi:10.1002/9783527641789.ch1
Kimura M et al (2005) Nanoscopic mechanism of protective rust formation on weathering steel surfaces. Nippon Steel Tech Rep 91:86–90
Kaiser MS, Shorowordi KM (2014) The influence of welding currents on the mechanical and physical properties of chromium-molybdenum steel. J Mech Eng 44(1):18–22
Peddle BE, Pickles CA (2000) Carbide and hardness development in the heat-affected zone of tempered and postweld heat-treated 2.25 Cr-1Mo steel weldments. J Mater Eng Perform 9(5):477–488
Xavier CR et al (2011) Numerical evaluation of the weldability of the low alloy ferritic steels T/P23 and T/P24. Mater Res 14(1):73–90