On the LiCo2/3Ni1/6Mn1/6O2 positive electrode material
English
Mahmoud, Abdelfattah mailto [Université de Liège - ULiège > Département de chimie (sciences) > LCIS - GreenMAT >]
Saadoune, Ismael [> >]
Amarilla, José Manuel [> >]
Hakkou, Rachid [> >]
2011
Electrochimica Acta
Pergamon Press - An Imprint of Elsevier Science
56
11
4081 - 4086
Yes (verified by ORBi)
International
0013-4686
[en] Lithium-ion batteries ; Layered oxide ; Combustion method ; LiCoNiMnO
[en] Abstract LiCo2/3Ni1/6Mn1/6O2 layered oxide was synthesized by the combustion method that led to a crystalline phase with good homogeneity and low particles size. The structural properties of the prepared positive electrode material were investigated by performing XRD Rietveld refinement. Practically no Li/Ni mixing was detected evidencing that the studied compound adopts almost an ideal α-NaFeO2 type structure. The Li||LiCo2/3Ni1/6Mn1/6O2 cell showed a discharge capacity of 199mAhg−1 when cycled in the 2.7–4.6V potential range while the best cycling performances were recorded when the upper cut off is fixed at 4.5V. Structural changes in LixCo2/3Ni1/6Mn1/6O2 with lithium electrochemical de-intercalation were studied using X-ray diffraction. This study clearly shows the existence of a solid solution domain in the 0.1<x<1.0 composition range while for x=0.1, a new phase appears explaining the decrease of the electrochemical performance when the cell is cycled at high upper cut off voltage.
CNRST Morocco/CSIC Spain (project 2010-2011)
Researchers ; Professionals ; Students
http://hdl.handle.net/2268/218228
https://doi.org/10.1016/j.electacta.2011.01.118
http://www.sciencedirect.com/science/article/pii/S0013468611001927

File(s) associated to this reference

Fulltext file(s):

FileCommentaryVersionSizeAccess
Restricted access
1-s2.0-S0013468611001927-main(2).pdfPublisher postprint979.12 kBRequest copy

Bookmark and Share SFX Query

All documents in ORBi are protected by a user license.