Polylactide (PLA) designed with desired end-use properties: 1. PLA compositions with low molecular weight ester-like plasticizers and related performances
Murariu, Marius; Da Silva Ferreira, Amalia; Alexandre, Michaëlet al.
2008 • In Polymers for Advanced Technologies, 19 (6), p. 636-646
[en] Polylactide (PLA) is an attractive candidate for replacing petrochemical polymers because it is
biodegradable and produced from annually renewable resources. Characterized by high tensile
strength, unfortunately the brittleness and rigidity of PLA limit its applicability. For a great number of applications such as packaging, fibers, films, etc., it is of high interest to formulate new grades with improved flexibility and better impact properties. In this objective, a specific PLA grade (L/D isomer ratio of 96:4, high molecular weight) was melt-mixed with selected plasticizers: bis(2-ethylhexyl) adipate (DOA), glyceryl triacetate (GTA), and tributyl O-acetylcitrate (TBAC). Their effect on the molecular, thermal, and mechanical properties of PLA was investigated for content up to 20wt% plasticizer and the results were correlated with a particular attention to the relationship between
property and application. Using the solubility and interaction parameters, a tentative evaluation of the product that could act as the most effective plasticizer for PLA has been performed and the obtained results have been corroborated with the materials physical properties. Excellent mechanical performances were obtained using the plasticizer having the lowest molecular mass (GTA) and the best interaction parameter. In relation to plasticizer amount/nature, the glass transition temperature of PLA (62-C) is decreased by plasticizing by more than 30-C, whereas better impact properties and lower stiffness are measured. The optimal formulations targeted to the final applications are clearly characterized by specific end-use properties: improved crystallization rates (PLA-DOA); high elongation at break and tensile strength (PLA-GTA, PLA-TBAC), medium to high impact properties (PLA-DOA, PLA-GTA) compositions.
Disciplines :
Chemistry
Author, co-author :
Murariu, Marius; Université de Mons-Hainaut - UMH > Center of Innovation and Research in Materials and Polymers (CIRMAP) > Laboratory of Polymeric and Composite Materials (LPCM)
Da Silva Ferreira, Amalia; Université de Mons-Hainaut - UMH > Center of Innovation and Research in Materials and Polymers (CIRMAP) > Laboratory of Polymeric and Composite Materials (LPCM)
Alexandre, Michaël ; Université de Mons-Hainaut - UMH > Center of Innovation and Research in Materials and Polymers (CIRMAP) > Laboratory of Polymeric and Composite Materials (LPCM)
Dubois, Philippe; Université de Mons-Hainaut - UMH > Center of Innovation and Research in Materials and Polymers (CIRMAP) > Laboratory of Polymeric and Composite Materials (LPCM)
Language :
English
Title :
Polylactide (PLA) designed with desired end-use properties: 1. PLA compositions with low molecular weight ester-like plasticizers and related performances
Publication date :
2008
Journal title :
Polymers for Advanced Technologies
ISSN :
1042-7147
eISSN :
1099-1581
Publisher :
John Wiley & Sons, Hoboken, United States - New Jersey
Drumright RE, Gruber PR, Henton DE. Polylactic acid technology. Adv. Mater. 2000; 12: 1841-1846.
Auras R, Harte B, Selke S. An overview of polylactides as packaging materials. Macromol. Biosci. 2004; 4: 835-864.
Vink ETH, Ràbago KR, Glassner DA, Gruber PR. Applications of life cycle assessment to NatureWork™ polylactide (PLA) production. Polym. Degrad. Stab. 2003; 80: 403-419.
Degée Ph, Dubois Ph. Recent advances in polylactide chemistry and materials science. In Encyclopedia of Chemical Technology (on line edn), Kirk-Othmer, (ed). John Wiley & Sons: Hoboken, NJ, 2004.
Mecking S. Nature or petrochemistry? - Biologically degradable materials. Angew. Chem. Int. Ed. 2004; 43: 1078-1085.
Hall ES, Kolstad JJ, Conn RSE, Gruber PR, Ryan CM. US patent no. 6355772, 2002.
Sinclair RG. US patent no. 5180765, 1993.
Jacobsen S, Fritz HG. Plasticizing polylactide - the effect of different plasticizers on the mechanical properties. Polym. Eng. Sci. 1999; 39: 1303-1310.
Martin O, Averous L. Poly(lactic acid): plasticization and properties of biodegradable multiphase systems. Polymer 2001; 42: 6209-6219.
Hiltunen E, Selin JF, Skog M. US patent no. 6117928, 2000.
Oksman K, Skrifvars M, Selin JF. Natural fibres as reinforcement in polylactic acid (PLA) composites. Comp. Sci. Tech. 2003; 63: 1317-1324.
Ljungberg N, Andersson T, Wesslen B. Film extrusion and film weldability of poly(lactic acid) plasticized with triacetine and tributyl citrate. J. Appl. Polym. Sci. 2003; 88: 3239-3247.
Baiardo M, Frisoni G, Scandola M, Rimelen M, Lips D, Ruffieux K, Winternantel E. Thermal and mechanical properties of plasticized poly(L)lactic acid. J. Appl. Polym. Sci. 2003; 90: 1731-1738.
Ljungberg N, Wesslen B. Preparation and properties of plasticized poly(lactic acid) films. Biomacromolecules 2005; 6: 1789-1796.
Ljungberg N, Wesslen B. Tributyl citrate oligomers as plasticizers for poly(lactic acid): thermo-mechanical film properties and aging. Polymer 2003; 44: 7679-7688.
Chen X, Schilling KH, Kelly WE. US patent no. 5756651, 1998.
Paul M-A, Alexandre M, Degée P, Henrist C, Rulmont A, Dubois P. New nanocomposite materials based on plasticized poly(L-lactide) and organo-modified montmorillonites: thermal and morphological study. Polymer 2003; 44: 443-450.
Hu Y, Hu YS, Topolkaraev V, Hiltner A, Baer E. Crystallization and phase separation in blends of high stereoregular poly(lactide) with poly(ethylene glycol). Polymer 2003; 44: 5681-5689.
Kulinski Z, Piorkowska E, Gadzinowska K, Stasiak M. Plasticization of poly(L-lactide) with poly(propylene glycol). Biomacromolecules 2006; 7: 2128-2135.
Murariu M, Da Silva Ferreira A, Degée P, Alexandre M, Dubois P. Polylacticle compositions. Part 1: effect of filler content and size on mechanical properties of PLA/calcium sulfate composites. Polymer 2007; 48: 2613-2618.
Fisher EW, Sterzel HJ, Wegner G. Investigation of the structure of solution grown crystals of lactide copolymers by means of chemical reactions. Colloid. Polym. Sci. 1973; 251: 980-990.
Ritchie PD (ed). Plasticisers, Stabilisers, and Fillers. Published for The Plastic Institute, London Iliffe Books Ltd: London, 1972.
Brandrup J, Immergut EH, Grulke EA (eds). Polymer Handbook, (4th edn), VII/675-711. John Wiley & Sons Inc.: New York, 1999.
Pilin I, Montrelay N, Grohens Y. Thermo-mechanical characterization of plasticized PLA: is the miscibility the only significant factor? Polymer 2006; 47: 4676-4682.
Peppas N, Branon-Peppas L. Controlled release of fragrances from polymers: I. Thermodynamic analysis. J. Control. Release 1996; 40: 245-250.
Eichie F, Okor RS, Groning R. Limitation observed in the application of the three dimensional solubility parameters to the coating formulation of poly (3-hydroxybutyrate-hydroxyvalerate) systems. Trop. J. Pharm. Res. 2005; 4: 355-362.
Sutinen R, Somppi M, Paronen P, Poso A. Predicting plasticization efficiency from three-dimensional molecular structure of a polymer plasticizer. Pharmacol. Res. 2001; 18: 1760-1766.
Pluta M. Morphology and properties of polylactide modified by thermal treatment, filling with layered silicates and plasticization. Polymer 2004; 45: 8239-8251.