Critical current; electric variables measurement; HTS tapes; magnetic susceptibility; superconducting fault current limiter
Abstract :
[en] Several high temperature superconductor (HTS) tapes have been developed since the late eighties. Due to the new techniques applied for their production, HTS tapes are becoming feasible and practical for many applications. In this work, we present the test results of five commercial HTS tapes from the BSCCO and YBCO families (short samples of 200 mm). We have measured and analyzed their intrinsic and extrinsic properties and compared their behaviors for fault current limiter (FCL) applications. Electrical measurements were performed to determine the critical current and the n value through the V-I relationship under DC and AC magnetic fields. The resistance per unit length was determined as a function of temperature. The magnetic characteristics were analyzed through susceptibility curves as a function of temperature. As transport current generates a magnetic field surrounding the HTS material, the magnetic measurements indicate the magnetic field supported by the tapes under a peak current 1.5 times higher than the critical current, I(c). By pulsed current tests the recovery time and the energy/volume during a current fault were also analyzed. These results are in agreement with the data found in the literature giving the most appropriate performance conductor for a FCL device (I(peak) = 4 kA) to be used in a 220 V-60 Hz grid.
J. Bock et al., "Development and successful testing of MCPBSCCO 2212 components for a 10 MVA resistive fault current limiter," Supercond. Sci. Technol., vol. 17, pp. 122-126, 2004.
J. Bock et al., "CURL 10: Development and field-test of a 10 kV/10 MVA resistive current limiter based on bulk MCP-BSCCO 2212," IEEE Trans. Appl. Supercond., vol. 15, no. 2, pp. 1955-1960, 2005. (Pubitemid 40970100)
J. X. Jin et al., "Operating principle of a high Tc superconducting saturable magnetic core fault current limiter," Physica C, vol. 282-287, pp. 2643-2644, 1997. (Pubitemid 127390181)
M. Okada, "HTS high field magnets," IEEE Trans. Appl. Supercond., vol. 10, no. 1, pp. 462-465, 2000.
Y. Y. Xie, K. Tekletsadik, D. Hazelton, and V. Selvamanickam, "Second generation high-temperature superconducting wires for fault current limiter applications," IEEE Trans. Appl. Supercond., vol. 17, no. 2, pp. 1981-1985, 2007. (Pubitemid 47166308)
S. S. Kalsi and A. Malozemoff, "HTS fault current limiter concept," in IEEE Power Engineering Society General Meeting June 06-10, 2004, Denver, CO, 2004, pp. 1426-1430.
W. Prusseit et al., "Reel to reel coated conductor fabrication by evaporation," IEEE Trans. Appl. Supercond., vol. 16, no. 2, pp. 996-998, 2006.
M. W. Rupich et al., "The development of second generation HTS wire at American superconductor," IEEE Trans. Appl. Supercond., vol. 17, no. 2, pp. 3379-3382, 2007. (Pubitemid 47166598)
V. Selvamanickam et al., "Fabrication of biaxially-textured thick film Y-Ba-Cu-O superconductor by MOCVD on cube-textured metal substrates," in TMS Spring Meeting, Comm., USA, 1997, T052 [Online]. Available: http://www.superpower-inc.com/files/ T052+TMS+Selva.pdf
V. Selvamanickam et al., "High-current Y-Ba-Cu-O coated conductor using metal organic chemical-vapor deposition and ion-beam-assisted deposition," IEEE Trans. Appl. Supercond., vol. 11, no. 1, pp. 3379-3381, 2001. (Pubitemid 32512667)
S. Kreiskott et al., "Reel-to-reel preparation of ion-beam assisted deposition (IBAD)-MgO based coated conductors," Supercond. Sci. Technol., vol. 17, pp. 132-134, 2004.
D. Dimos, P. Chaudhari, and J. Mannhardt, "Superconducting transport properties of grain boundaries in YBa2Cu3O7 bicrystals," J. Phys. Rev. B, vol. 41, p. 4038, 1990.
C. R.Walter, "Brookhaven National Laboratory informal report," BNL 18928 AADD 74-2, January 30, 1974.
P. Bruzzone, "The index n of the voltage-current curve in the characterization and specification of technical superconductors," Physica C, vol. 401, no. 1-4, pp. 7-14, 2004.
"EHTS BSCCO data sheet," European High Temperature Superconductors GmbH & Co., Hanau, Germany, 2003.
T. Nakano and T. Hashimoto, "Refrigeration character of new-type Peltier refrigerator using high-Tc (Bi, Pb)2Sr2Ca 2Cu3Oy superconductor," Jpn. J. Appl. Phys., vol. 33, pp. 1728-1731, 1994.
J. H. Kim et al., "Characteristics of critical current and index n of Bi-2223/Ag tape up to 30 T at 4.2 K," IEEE Trans. Appl. Supercond., vol. 15, no. 2, pp. 2470-2473, 2005. (Pubitemid 40969926)
D. K. Park et al., "Development of 220 V/300 A class non-inductive winding type fault current limiter using 2G HTS wire," IEEE Trans. Appl. Supercond., vol. 17, no. 2, pp. 1863-1866, 2007. (Pubitemid 47166279)
M. C. Anh et al., "Recovery characteristics of resistive SFCL wound with YBCO coated conductor in a power system," IEEE Trans. Appl. Supercond., vol. 17, no. 2, pp. 1859-1862, 2007.
M.Vojenciak, J. Souc, F. Gömöry, and E. Seiler, "Influence ofDCmagnetic field on AC loss of YBCO coated conductor with ferromagnetic substrate," Polish Acad Sciences Inst Physics, pp. 359-362, 2008. (Pubitemid 351281474)
S. W. Yim, S. H. Lim, H. R. Kim, S. D. Hwang, and K. Kishio, "Electrical behaviour of Bi-2223/Ag tapes under applied alternating overcurrents," IEEE Trans. Appl. Supercond., vol. 15, no. 2, pp. 2482-2487, 2005. (Pubitemid 40963880)
W. Schmidt et al., "Investigation of YBCO coated conductors for fault current limiter applications," IEEE Trans. Appl. Supercond., vol. 17, no. 2, pp. 3471-3474, 2007. (Pubitemid 47166619)
J. F. Fagnard et al., "Intragranular and intergranular behaviour of multifilamentary Bi-2223/Ag tapes," Physica C, vol. 372, pp. 970-973, 2002.
C. A. Baldan, J. S. Lamas, C. Y. Shigue, and E. Ruppert Filho, "Fault current limiter using YBCO coated conductor-The limiting factor and its recovery time," IEEE Trans. Appl. Supercond., vol. 19, no. 3, pp. 1810-1813, 2009.